High-pressure die cast (HPDC) AZ91 magnesium alloy is widely used in automotive components such as transmission housings and brackets for its excellent strength-to-weight ratio. Zinc-based cold spray coatings can be applied selectively to vulnerable areas to enhance corrosion resistance, minimize galvanic coupling with dissimilar metals, and eliminate the need for full-surface oxide coatings, making the process more efficient and targeted. A comprehensive evaluation of 16 combinations of nitrogen carrier gas temperatures and pressures led to the identification of an optimal range of process parameters, yielding Zn coatings with porosity <0.5% by area, wear rates reduced by a factor of two compared to uncoated AZ91, and adhesion strengths up to 35 MPa. The enhanced mechanical performance of the coating is attributed to the low porosity and the formation of a metallurgical bond at the coating-substrate interface. Corrosion studies using macroscale potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) revealed a significant decrease in corrosion rate and a shift to more noble corrosion potentials (ZCP) for coated substrates. Furthermore, the Zn cold-sprayed samples exhibited significantly lower corrosion-induced evolved hydrogen content compared to the base AZ91 substrate and AZ91 coated with industrial coatings, demonstrating that the Zn layer effectively protects the substrate from the corrosive environment. Overall, cold spray Zn coatings significantly improve the mechanical and corrosion performance of AZ91 Mg alloys, addressing key material challenges and enabling their broader use in automotive applications.

Magnesium (Mg) alloys are ideal candidates for automotive applications due to their high strength to weight ratio, castability, recyclability etc., however, they lack corrosion and oxidation resistance. Solid-state deposition techniques, such as cold spray, have been demonstrated to enhance their corrosion resistance as it relies on the severe plastic deformation of powder particles upon impact with the substrate to form a metallurgical bond with the substrate and within the coating. At cold sprayed interfaces, a heterogeneous microstructure is formed that includes some porosity, oxides and intermetallics which can significantly affect coating performance. Thus, establishing a direct correlation between the interface microstructure and its properties can aid in designing optimal cold spray parameters. In this study, we investigated the microstructure and mechanical properties of a zinc (Zn) coating deposited on a high pressure die cast (HPDC) AZ91 Mg substrate via high resolution scanning transmission electron microscopy, in situ micro-tensile testing, and finite element method (FEM) modeling. Micro-tensile pillars fabricated using the plasma focused ion beam (PFIB) successfully isolates the coating-substrate interface within the gauge length. The average bond strength of Zn-Mg interface was determined to be ~140 MPa with failure occurring partially at the interface and mostly into the coatings. A detailed microstructural characterization revealed evidence of a strong metallurgical bonding at the Zn-Mg interface and formation of the C14 MgZn₂ laves phase interlayer resulting in a mixed mode of fracture during the micro-tensile experiments. FEM modeling reveals the stress distribution along the interfaces and suggests that a MgZn₂ layer thickness between 200–400 nm is optimum to increase the bond strength and minimize the triaxiality. Such a site-specific interfacial analysis with correlative computational modeling provides crucial insight into the overall performance of cold spray interfaces.