In this study, a polypropylene (PP) matrix was reinforced with ultra-fine graphene nanoplatelets (GNPs), aluminum-carbon layered double hydroxides (Al-C LDHs), and calcium carbonate (CaCO₃) as hybrid reinforcements, along with polypropylene grafted maleic anhydride (PP-g-MA) compatibilizers to create a novel thermoplastic-based hybrid composite polymer. The hybrid composite consisted of varying weight percentages of GNPs (ranging from 0.5 to 2.0 wt% in increments of 0.5), 2wt% Al-C LDH, 2wt % CaCO₃, and 5wt % PP-g-MA. The bulk samples were manufactured using twin-screw extrusion followed by vertical injection molding. The developed hybrid composites were characterized using high-resolution scanning electron microscopy (HRSEM) for microstructural analysis, X-ray diffraction (XRD) for phase identification, X-ray photoelectron spectroscopy (XPS) for compositional analysis, and Fourier-transform infrared spectroscopy (FTIR) for functional group identification. Thermogravimetric analysis (TGA) was performed to assess thermal stability, crystallization, and melting behavior. Mechanical tests, including tensile, compressive, and three-point bending, were conducted to evaluate mechanical properties, while a low-velocity impact test assessed impact resistance. The results showed that the hybrid composite with a PP matrix embedded with 1.5 wt% GNPs, 2 wt% Al-C LDH, and 2 wt% CaCO₃ exhibited improved mechanical properties, achieving an ultimate tensile strength of approximately 45 MPa. This enhancement is attributed to the effective interconnection, bonding, and cross-linking of the reinforcements with the PP matrix, facilitating efficient load transfer, which makes it suitable for structural applications.

In this study, ultra-fine graphene nanoplatelets (GNPs) were employed as nanofillers to reinforce a polypropylene (PP) matrix. This was done in conjunction with a polypropylene grafted maleic anhydride (PP-MAH) compatibilizer and calcium carbonate (CaCO₃), with the aim of improving the mechanical and thermal properties of the resulting hybrid composites. Formulations for the hybrid composites were fabricated by compounding the PP matrix with varying weight percentages of GNPs (x = 0.5, 1.0, 1.5, 2.0), 2 wt.% CaCO₃, and 5 wt.% PP-MAH using a twin-screw extruder followed by injection molding. This research thoroughly investigates the mechanical and thermal characteristics. X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Fourier-transform infrared spectroscopy (FTIR) results confirm the successful development of hybrid composites. The thermal stability, crystallization temperature, melting temperature, tensile strength, flexural strength, and impact resistance were evaluated using differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), universal testing machine, and low-velocity impact tester, respectively. The results indicated a significant improvement in the tensile strength of the PP matrix with the addition of GNPs, with the highest enhancement observed at 1.5 wt.% GNP loading, where the tensile strength reached a maximum of 40.54 MPa. This improvement was attributed to the proper interconnection, bonding, and compounding of PP with GNPs, thus leading to an increase in the load transfer efficiency.