Entropy regulation in LaNbO₄-based fergusonite to implement high-temperature phase transition and promising dielectric properties

High-entropy effect is a novel design strategy to optimize properties and explore novel materials. In this work, (La_1/5Nd_1/5Sm_1/5Ho_1/5Y_1/5)NbO₄ (5RNO) high-entropy microwave dielectric ceramics were successfully prepared in the sintering temperature (S.T.) range of 1210–1290 ℃ via a solid-phase reaction route, and medium-entropy (La_1/3Nd_1/3Sm_1/3)NbO₄ and (La_1/4Nd_1/4Sm_1/4Ho_1/4)NbO₄ (3RNO and 4RNO) ceramics were compared. The effects of the entropy (S) on crystal structure, phase transition, and dielectric performance were evaluated. The entropy increase yields a significant increase in a phase transition temperature (from monoclinic fergusonite to tetragonal scheelite structure). Optimal microwave dielectric properties were achieved in the high-entropy ceramics (5RNO) at the sintering temperature of 1270 ℃ for 4 h with a relative density of 98.2% and microwave dielectric properties of dielectric permittirity (ε_r) = 19.48, quality factor (Q×f) = 47,770 GHz, and resonant frequency temperature coefficient (τ_f) = –13.50 ppm/℃. This work opens an avenue for the exploration of novel microwave dielectric material and property optimization via entropy engineering.