New two-layer Ruddlesden-Popper (RP) oxide La0.25Sr2.75FeNiO7-δ (LSFN) in the combination of Sr3Fe2O7-δ and La3Ni2O7-δ was successfully synthesized and studied as the potential active single-phase and composite cathode for protonic ceramics fuel cells (PCFCs). LSFN with the tetragonal symmetrical structure (I4/mmm) is confirmed, and the co-existence of Fe3+/Fe4+ and Ni3+/Ni2+ couples is demonstrated by X-ray photoelectron spectrometer (XPS) analysis. The LSFN conductivity is apparently enhanced after Ni doping in Fe-site, and nearly three times those of Sr3Fe2O7-δ, which is directly related to the carrier concentration and conductor mechanism. Importantly, anode supported PCFCs using LSFN-BaZr0.1Ce0.7Y0.2O3-δ (LSFN-BZCY) composite cathode achieved high power density (426 mW·cm-2 at 650 ℃) and low electrode interface polarization resistance (0.26 Ω·cm2). Besides, distribution of relaxation time (DRT) function technology was further used to analyse the electrode polarization processes. The observed three peaks (P1, P2, and P3) separated by DRT shifted to the high frequency region with the decreasing temperature, suggesting that the charge transfer at the electrode-electrolyte interfaces becomes more difficult at reduced temperatures. Preliminary results demonstrate that new two-layer RP phase LSFN can be a promising cathode candidate for PCFCs.


menu
Abstract
Full text
Outline
Electronic supplementary material
About this article

New two-layer Ruddlesden-Popper cathode materials for protonic ceramics fuel cells

Show Author's information Yihan LING( )Tianming GUOYangyang GUOYang YANGYunfeng TIANXinxin WANGXuemei OUPeizhong FENG
School of Materials Science and Physics, China University of Mining and Technology, Xuzhou 221116, China

Abstract

New two-layer Ruddlesden-Popper (RP) oxide La0.25Sr2.75FeNiO7-δ (LSFN) in the combination of Sr3Fe2O7-δ and La3Ni2O7-δ was successfully synthesized and studied as the potential active single-phase and composite cathode for protonic ceramics fuel cells (PCFCs). LSFN with the tetragonal symmetrical structure (I4/mmm) is confirmed, and the co-existence of Fe3+/Fe4+ and Ni3+/Ni2+ couples is demonstrated by X-ray photoelectron spectrometer (XPS) analysis. The LSFN conductivity is apparently enhanced after Ni doping in Fe-site, and nearly three times those of Sr3Fe2O7-δ, which is directly related to the carrier concentration and conductor mechanism. Importantly, anode supported PCFCs using LSFN-BaZr0.1Ce0.7Y0.2O3-δ (LSFN-BZCY) composite cathode achieved high power density (426 mW·cm-2 at 650 ℃) and low electrode interface polarization resistance (0.26 Ω·cm2). Besides, distribution of relaxation time (DRT) function technology was further used to analyse the electrode polarization processes. The observed three peaks (P1, P2, and P3) separated by DRT shifted to the high frequency region with the decreasing temperature, suggesting that the charge transfer at the electrode-electrolyte interfaces becomes more difficult at reduced temperatures. Preliminary results demonstrate that new two-layer RP phase LSFN can be a promising cathode candidate for PCFCs.

Keywords: charge transfer, protonic ceramics fuel cells (PCFCs), Ruddlesden-Popper (RP) phase, single-phase cathode, distribution of relaxation time (DRT) function

References(40)

[1]
Radenahmad N, Afif A, Petra PI, et al. Proton-conducting electrolytes for direct methanol and direct urea fuel cells-A state-of-the-art review. Renew Sustain Energy Rev 2016, 57: 1347-1358.
[2]
Duan CC, Kee RJ, Zhu HY, et al. Highly durable, coking and sulfur tolerant, fuel-flexible protonic ceramic fuel cells. Nature 2018, 557: 217-222.
[3]
Bonanos N, Huijser A, Poulsen FW. H/D isotope effects in high temperature proton conductors. Solid State Ion 2015, 275: 9-13.
[4]
Wang XX, Wei KW, Yan SL, et al. Efficient and stable conversion of oxygen-bearing low-concentration coal mine methane by the electrochemical catalysis of SOFC anode: From pollutant to clean energy. Appl Catal B: Environ 2020, 268: 118413.
[5]
Yang L, Zuo CD, Wang SZ, et al. A novel composite cathode for low-temperature SOFCs based on oxide proton conductors. Adv Mater 2008, 20: 3280-3283.
[6]
Yang Y, Bao H, Ni H, et al. A novel facile strategy to suppress Sr segregation for high-entropy stabilized La0.8Sr0.2MnO3-δ cathode. J Power Sources 2021, 482: 228959.
[7]
Shao ZP, Haile SM. A high-performance cathode for the next generation of solid-oxide fuel cells. Nature 2004, 431: 170-173.
[8]
Tarutin AP, Lyagaeva JG, Medvedev DA, et al. Recent advances in layered Ln2NiO4+δ nickelates: Fundamentals and prospects of their applications in protonic ceramic fuel and electrolysis cells. J Mater Chem A 2021, 9: 154-195.
[9]
Dong FF, Chen DJ, Ran R, et al. A comparative study of Sm0.5Sr0.5MO3-δ (M = Co and Mn) as oxygen reduction electrodes for solid oxide fuel cells. Int J Hydrog Energy 2012, 37: 4377-4387.
[10]
Nie LF, Liu MF, Zhang YJ, et al. La0.6Sr0.4Co0.2Fe0.8O3-δ cathodes infiltrated with samarium-doped cerium oxide for solid oxide fuel cells. J Power Sources 2010, 195: 4704-4708.
[11]
Zhou W, Shao ZP, Ran R, et al. A novel efficient oxide electrode for electrocatalytic oxygen reduction at 400-600 ℃. Chem Commun 2008: 5791-5793.
[12]
Leng YJ, Chan SH, Liu QL. Development of LSCF-GDC composite cathodes for low-temperature solid oxide fuel cells with thin film GDC electrolyte. Int J Hydrog Energy 2008, 33: 3808-3817.
[13]
Xia CR, Rauch W, Chen FL, et al. Sm0.5Sr0.5CoO3 cathodes for low-temperature SOFCs. Solid State Ion 2002, 149: 11-19.
[14]
Xu X, Xu YS, Ma JM, et al. Tailoring electronic structure of perovskite cathode for proton-conducting solid oxide fuel cells with high performance. J Power Sources 2021, 489: 229486.
[15]
Nirala G, Yadav D, Upadhyay S. Ruddlesden-Popper phase A2BO4 oxides: Recent studies on structure, electrical, dielectric, and optical properties. J Adv Ceram 2020, 9: 129-148.
[16]
Beppu K, Hosokawa S, Teramura K, et al. Oxygen storage capacity of Sr3Fe2O7-δ having high structural stability. J Mater Chem A 2015, 3: 13540-13545.
[17]
Yashima M, Enoki M, Wakita T, et al. Structural disorder and diffusional pathway of oxide ions in a doped Pr2NiO4-based mixed conductor. J Am Chem Soc 2008, 130: 2762-2763.
[18]
Tarancón A, Skinner SJ, Chater RJ, et al. Layered perovskites as promising cathodes for intermediate temperature solid oxide fuel cells. J Mater Chem 2007, 17: 3175-3181.
[19]
Patrakeev MV, Leonidov IA, Kozhevnikov VL, et al. Ion-electron transport in strontium ferrites: Relationships with structural features and stability. Solid State Sci 2004, 6: 907-913.
[20]
Ling Y, Wang F, Budiman RA, et al. Oxygen nonstoichiometry, the defect equilibrium model and thermodynamic quantities of the Ruddlesden-Popper oxide Sr3Fe2O7-δ. Phys Chem Chem Phys 2015, 17: 7489-7497.
[21]
Wang ZQ, Yang WQ, Shafi SP, et al. A high performance cathode for proton conducting solid oxide fuel cells. J Mater Chem A 2015, 3: 8405-8412.
[22]
Ling YH, Guo TM, Zhang XZ, et al. Evaluation of electrical conductivity and oxygen diffusivity of the typical Ruddlesden-Popper oxide Sr3Fe2O7-δ. Ceram Int 2017, 43: 16264-16269.
[23]
Mogni L, Prado F, Ascolani H, et al. Synthesis, crystal chemistry and physical properties of the Ruddlesden-Popper phases Sr3Fe2-xNixO7-δ (0 ≤ x ≤ 1.0). J Solid State Chem 2005, 178: 1559-1568.
[24]
Mogni L, Prado F, Caneiro A. Defect structure and electrical conductivity of the Ruddlesden-Popper phases Sr3FeMO6+δ (M = Co, Ni). Chem Mater 2006, 18: 4163-4170.
[25]
Ling YH, Wang F, Okamoto Y, et al. Oxygen nonstoichiometry and thermodynamic quantities in the Ruddlesden-Popper oxides LaxSr3-xFe2O7-δ. Solid State Ion 2016, 288: 298-302.
[26]
Ling YH, Wang F, Okamoto Y, et al. Oxygen nonstoichiometry and thermodynamic explanation of large oxygen-deficient ruddlesden-popper oxides LaxSr3-xFe2O7-δ. J Am Ceram Soc 2016, 99: 3792-3801.
[27]
Yoo S, Choi S, Shin J, et al. Electrical properties, thermodynamic behavior, and defect analysis of Lan+1NinO3n+1+d infiltrated into YSZ scaffolds as cathodes for intermediate-temperature SOFCs. RSC Adv 2012, 2: 4648-4655.
[28]
Amow G, Davidson IJ, Skinner SJ. A comparative study of the Ruddlesden-Popper series, Lan+1NinO3n+1 (n = 1, 2 and 3), for solid-oxide fuel-cell cathode applications. Solid State Ion 2006, 177: 1205-1210.
[29]
Chen ZZ, Wang JL, Huan DM, et al. Tailoring the activity via cobalt doping of a two-layer Ruddlesden-Popper phase cathode for intermediate temperature solid oxide fuel cells. J Power Sources 2017, 371: 41-47.
[30]
Yang Y, Chen YH, Tian D, et al. A new A-site excessive strategy to improve performance of layered perovskite cathode for intermediate-temperature solid oxide fuel cells. Electrochimica Acta 2017, 231: 686-693.
[31]
Velázquez-Palenzuela A, Zhang L, Wang LC, et al. Carbon-supported Fe-Nx catalysts synthesized by pyrolysis of the Fe(II)-2,3,5,6-tetra(2-pyridyl)pyrazine complex: Structure, electrochemical properties, and oxygen reduction reaction activity. J Phys Chem C 2011, 115: 12929-12940.
[32]
Xiao GL, Liu Q, Wang SW, et al. Synthesis and characterization of Mo-doped SrFeO3-δ as cathode materials for solid oxide fuel cells. J Power Sources 2012, 202: 63-69.
[33]
Dai NN, Feng J, Wang ZH, et al. Synthesis and characterization of B-site Ni-doped perovskites Sr2Fe1.5-xNixMo0.5O6-δ (x = 0, 0.05, 0.1, 0.2, 0.4) as cathodes for SOFCs. J Mater Chem A 2013, 1: 14147-14153.
[34]
Kang HW, Lim SN, Park SB. Co-doping schemes to enhance H2 evolution under visible light irradiation over SrTiO3:Ni/M (M = La or Ta) prepared by spray pyrolysis. Int J Hydrog Energy 2012, 37: 5540-5549.
[35]
Lu YX, Jiang Y, Yang Z, et al. Polymer-assisted synthesis of LiNi2/3Mn1/3O2 cathode material with enhanced electrochemical performance. J Alloys Compd 2013, 559: 203-208.
[36]
Sun WP, Shi Z, Fang SM, et al. A high performance BaZr0.1Ce0.7Y0.2O3-δ-based solid oxide fuel cell with a cobalt-free Ba0.5Sr0.5FeO3-δ-Ce0.8Sm0.2O2-δ composite cathode. Int J Hydrog Energy 2010, 35: 7925-7929.
[37]
Fuoss RM, Kirkwood JG. Electrical properties of solids. VIII. Dipole moments in polyvinyl chloride-diphenyl systems. J Am Chem Soc 1941, 63: 385-394.
[38]
Shi N, Su F, Huan DM, et al. Performance and DRT analysis of P-SOFCs fabricated using new phase inversion combined tape casting technology. J Mater Chem A 2017, 5: 19664-19671.
[39]
Xu H, Dang Z. Numerical investigation of coupled mass transport and electrochemical reactions in porous SOFC anode microstructure. Int J Heat Mass Transf 2017, 109: 1252-1260.
[40]
Wang X, Ma Z, Zhang T, et al. Charge-transfer modeling and polarization DRT analysis of proton ceramics fuel cells based on mixed conductive electrolyte with the modified anode-electrolyte interface. ACS Appl Mater Inter 2018, 10: 35047-35059.
File
40145_2021_488_MOESM1_ESM.pdf (323.4 KB)
Publication history
Copyright
Acknowledgements
Rights and permissions

Publication history

Received: 01 February 2021
Revised: 15 April 2021
Accepted: 27 April 2021
Published: 15 September 2021
Issue date: October 2021

Copyright

© The Author(s) 2021

Acknowledgements

This work was financially supported by the Fundamental Research Funds for the Central Universities (No. 2019GF10).

Rights and permissions

This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.

The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.

To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Return