Electrochemical nitric oxide reduction reaction (NORR) to produce ammonia (NH3) under ambient conditions is a promising alternative to the energy and carbon-intensive Haber–Bosch approach, but its performance is still improved. Herein, molybdenum carbides (MoC) nanocrystals confined by nitrogen-doped carbon nanosheets are first designed as an efficient and durable electrocatalyst for catalyzing the reduction of NO to NH3 with maximal Faradaic efficiency of 89% ± 2% and a yield rate of 1,350 ± 15 μg·h−1·cm−2 at the applied potential of −0.8 V vs. reversible hydrogen electrode (RHE) as well as high stable activity with negligible current density and NH3 yield rate decays over a 30 h continue the test. Moreover, as a proof-of-concept of Zn–NO battery, it achieves a peak power density of 1.8 mW·cm−2 and a large NH3 yield rate of 782 ± 10 μg·h−1·cm−2, which are comparable to the best-reported results. Theoretical calculations reveal that the MoC(111) has a strong electronic interaction with NO molecules and thus lowering the energy barrier of the potential-determining step and suppressing hydrogen evolution kinetics. This work suggests that Mo-based materials are a powerful platform providing great opportunities to explore highly selective and active catalysts for NH3 production.

File
12274_2022_4747_MOESM1_ESM.pdf (2.2 MB)
Publication history
Copyright
Acknowledgements

Publication history

Received: 20 May 2022
Revised: 24 June 2022
Accepted: 07 July 2022
Published: 18 August 2022
Issue date: October 2022

Copyright

© Tsinghua University Press 2022

Acknowledgements

Acknowledgements

This work was financially supported by National Natural Science Foundation of China (Nos. 22075211, 22109118, 21601136, 51971157, and 51621003).

Return