Full Length Article | Open Access

Texture traits and mechanical anisotropy of AZ31 magnesium alloy sheet by hard plate cross rolling

Jia Yang ZhangaFeng Lia,b,c( )Lu Suna( )Wen Tao NiuaMu Zi Caoa
School of Materials Science and Chemical Engineering, Harbin University of Science and Technology, Harbin 150040, PR China
Key Laboratory of Advanced Manufacturing and Intelligent Technology, Ministry of Education, Harbin University of Science and Technology, Harbin 150080, PR China
Heilongjiang Provincial Key Laboratory of Light Metal Materials Modification & Green Forming Technology, Harbin University of Science and Technology, Harbin 150040, PR China
Show Author Information

Abstract

Conventional cross rolling is influenced by the force couple effect of symmetrical rollers, resulting in the c-axis of the plate grains being oriented perpendicular to the rolling surface. This orientation contributes to a high degree of work hardening and mechanical anisotropy, thereby complicating subsequent processing. In this study, the hard plate cross rolling (HP-CR) process is put forward for the first time, and the microstructure evolution and mechanical properties of rolled AZ31 Magnesium plate were analyzed. The results indicate that, in comparison to traditional cross rolling (CR), the average grain size of the HP-CR is refined to 5.33 µm. Additionally, the average yield strength and elongation of the sheet are enhanced by 15.2 % and 35.2 %, respectively, while the average tensile strength is 283 MPa, and the r value decreases by 39.8 %. These changes are attributed to the combined effects of grain refinement, microstructural homogenization, and basal texture weakening. On the one hand, the substantial energy stored in the original lattice distortion serves as a driving force for the dynamic recrystallization process, facilitating the elimination of the deformed grain structure. This process increases the proportion of recrystallized grains from 5 % to 82 %, reduces the degree of work hardening, and correspondingly decreases the density of geometrically necessary dislocations (ρGND) by 70.8 %, accompanied by the formation of high-angle grain boundaries (HAGB). On the other hand, dynamic recrystallization promotes grain rearrangement, resulting in an increased number of grains oriented in the transverse direction (TD), which diminishes the texture strength of the basal plane. Concurrently, the activation of non-basal slip systems reduces the resistance to dislocation sliding in various directions, significantly reduces the degree of mechanical anisotropy and enhancing the plastic deformation capacity of the plate. This research provides valuable scientific insights and technical foundations for the large-scale manufacturing of high-performance AZ31 magnesium alloy sheets.

References

【1】
【1】
 
 
Journal of Magnesium and Alloys

{{item.num}}

Comments on this article

Go to comment

< Back to all reports

Review Status: {{reviewData.commendedNum}} Commended , {{reviewData.revisionRequiredNum}} Revision Required , {{reviewData.notCommendedNum}} Not Commended Under Peer Review

Review Comment

Close
Close
Cite this article:
Zhang JY, Li F, Sun L, et al. Texture traits and mechanical anisotropy of AZ31 magnesium alloy sheet by hard plate cross rolling. Journal of Magnesium and Alloys, 2026, 14(C). https://doi.org/10.1016/j.jma.2025.01.004

4

Views

0

Downloads

0

Crossref

0

Web of Science

0

Scopus

0

CSCD

Received: 25 September 2024
Revised: 26 December 2024
Accepted: 13 January 2025
Published: 30 January 2025
© 2026 Chongqing University.

This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/)