Hydrogen Adsorption on Metal-Organic Framework MOF-177

This review summarizes the recent literature on the synthesis, characterization, and adsorption properties of meal-organic framework MOF-177. MOF-177 is a porous crystalline material that consists of Zn₄O tetrahedrons connected with benzene tribenzoate (BTB) ligands. It is an ideal adsorbent with an exceptionally high specific surface area (BET>4500 m²/g), a uniform micropore size distribution with a median pore diameter of 12.7 Å, a large pore volume (2.65 cm³/g), and very promising adsorption properties for hydrogen storage and other gas separation and purification applications. A hydrogen adsorption amount of 19.6 wt.% on MOF-177 at 77 K and 100 bar was observed, and a CO₂ uptake of 35 mmol/g on MOF-177 was measured at 45 bar and an ambient temperature. Other hydrogen properties (kinetics and heat of adsorption) along with adsorption of other gases including CO₂, CO, CH₄, and N₂O on MOF-177 were also be discussed. It was observed in experiments that MOF-177 adsorbent tends to degrade or decompose when it is exposed to moisture. Thermogravimetric analysis showed that the structure of MOF-177 remains intact at temperatures below 330℃ under a flow of oxygen, but decomposes to zinc oxide at 420℃.