Journal Home > Volume 12 , Issue 5
Friction 2024, 12(5): 997-1015 https://doi.org/10.1007/s40544-023-0824-9
Research Article | Open Access | Issue | Published: 04 December 2023

Mechanisms behind the environmental sensitivity of carbon fiber reinforced polytetrafluoroethylene (PTFE)

Show Author's Information Pontus JOHANSSON( ),  P. MARKLUND,  M. BJÖRLING,  Y. SHI
Division of Machine Element, Luleå University of Technology, Luleå SE-97187, Sweden
Keywords:
polymer composite, tribofilm, tribochemistry, atmosphere
Cite this article:
JOHANSSON P, MARKLUND P, BJÖRLING M, et al. Mechanisms behind the environmental sensitivity of carbon fiber reinforced polytetrafluoroethylene (PTFE). Friction, 2024, 12(5): 997-1015. https://doi.org/10.1007/s40544-023-0824-9
Download citation
EndNote(RIS)
BibTeX

167

Views

6

Downloads

Citations

1

Crossref

1

WoS

1

Scopus

0

CSCD

Abstract Full text About this article

Carbon fiber reinforced polytetrafluoroethylene (CF/PTFE) composites are known for their exceptional tribological performance when sliding against steel or cast iron in inert gas environments. Compared to experiments in humid air, about an order of magnitude lower wear rate and several times lower coefficient of friction have been reported for tests conducted in dry nitrogen and hydrogen. Moreover, trace moisture has been shown to affect the friction and wear significantly of this tribosystem, although a possible effect of oxygen cannot be ruled out due to uncertainties regarding the oxygen concentrations. While several studies have pointed out the environmental sensitivity of CF/PTFE, the understanding of the underlying mechanisms are very limited. The objective of this research is to investigate the individual and combined effect of oxygen and moisture on the tribological behavior of CF/PTFE sliding against steel. Additionally, this study aims to elucidate the underlying mechanisms that govern the environmental sensitivity of the system. Climate-controlled three-pin-on-disc experiments were conducted in nitrogen atmospheres at various concentrations of oxygen and moisture. The tribological results clearly demonstrate that both moisture and oxygen contribute to increased friction and wear. However, the adverse effect was much more pronounced for oxygen than moisture. A qualitative method was developed to estimate the tribofilm coverage on the CF/PTFE surface. Results showed strong correlation between high coverage of strongly adhered tribofilm and low wear rate. Moreover, a loosely adhered tribofilm was observed on top of the CF/PTFE surface in presence of moisture. FTIR analysis indicated that the loosely adhered tribofilm found in the moisture-enriched environment contained a significant amount of adsorbed water, which may explain the lower coefficient of friction in presence of moisture compared to oxygen. The adsorbed water in the loosely adhered tribofilm could be an indication of moisture-driven lubrication by the non-graphitic carbon in the tribofilm.


menu
Abstract
Full text
Outline
About this article

Mechanisms behind the environmental sensitivity of carbon fiber reinforced polytetrafluoroethylene (PTFE)

Show Author's information Pontus JOHANSSON( ), P. MARKLUND, M. BJÖRLING, Y. SHI
Division of Machine Element, Luleå University of Technology, Luleå SE-97187, Sweden

Abstract

Carbon fiber reinforced polytetrafluoroethylene (CF/PTFE) composites are known for their exceptional tribological performance when sliding against steel or cast iron in inert gas environments. Compared to experiments in humid air, about an order of magnitude lower wear rate and several times lower coefficient of friction have been reported for tests conducted in dry nitrogen and hydrogen. Moreover, trace moisture has been shown to affect the friction and wear significantly of this tribosystem, although a possible effect of oxygen cannot be ruled out due to uncertainties regarding the oxygen concentrations. While several studies have pointed out the environmental sensitivity of CF/PTFE, the understanding of the underlying mechanisms are very limited. The objective of this research is to investigate the individual and combined effect of oxygen and moisture on the tribological behavior of CF/PTFE sliding against steel. Additionally, this study aims to elucidate the underlying mechanisms that govern the environmental sensitivity of the system. Climate-controlled three-pin-on-disc experiments were conducted in nitrogen atmospheres at various concentrations of oxygen and moisture. The tribological results clearly demonstrate that both moisture and oxygen contribute to increased friction and wear. However, the adverse effect was much more pronounced for oxygen than moisture. A qualitative method was developed to estimate the tribofilm coverage on the CF/PTFE surface. Results showed strong correlation between high coverage of strongly adhered tribofilm and low wear rate. Moreover, a loosely adhered tribofilm was observed on top of the CF/PTFE surface in presence of moisture. FTIR analysis indicated that the loosely adhered tribofilm found in the moisture-enriched environment contained a significant amount of adsorbed water, which may explain the lower coefficient of friction in presence of moisture compared to oxygen. The adsorbed water in the loosely adhered tribofilm could be an indication of moisture-driven lubrication by the non-graphitic carbon in the tribofilm.

Keywords: polymer composite, tribofilm, tribochemistry, atmosphere

References(66)

[1]
Dhanumalayan E, Joshi G M. Performance properties and applications of polytetrafluoroethylene (PTFE)—A review. Adv Compos Hybrid Mater 1(2): 247–268 (2018)
DOI Google Scholar
[2]
Friedrich K, Chang L, Haupert F. Current and future applications of polymer composites in the field of tribology. In: Composite Materials. London: Springer, 2011: 129–167.
DOI
[3]
Radcliffe C. Sealing material developments for reciprocating gas compressors. Seal Technol 2005(11): 7–11 (2005)
DOI Google Scholar
[4]
Wang F K. (2017) Carbon fibers and their thermal transporting properties. In: Thermal Transport in Carbon-Based Nanomaterials. Amsterdam: Elsevier: 135–184
DOI
[5]
Newcomb B A. Processing, structure, and properties of carbon fibers. Compos Part A Appl Sci Manuf 91: 262–282 (2016)
DOI Google Scholar
[6]
Lancaster J K. The effect of carbon fibre reinforcement on the friction and wear of polymers. J Phys D: Appl Phys 1(5): 549–559 (1968)
DOI Google Scholar
[7]
Tanaka K. Friction and wear of glass and carbon fiber-filled thermoplastic polymers. J Lubr Technol 99(4): 408–414 (1977)
DOI Google Scholar
[8]
Tanaka K, Yamada Y. Influence of counterface roughness on the friction and wear of polytetrafluorethylene- and polyacetal-based composites. J Synth Lubr 5(2): 115–131 (1988)
DOI Google Scholar
[9]
Bijwe J, Neje S, Indumathi J, Fahim M. Friction and wear performance evaluation of carbon fibre reinforced PTFE composite. J Reinf Plast Compos 21(13): 1221–1240 (2002)
DOI Google Scholar
[10]
Sawae Y, Morita T, Takeda K, Onitsuka S, Kaneuti J, Yamaguchi T, Sugimura J. Friction and wear of PTFE composites with different filler in high purity hydrogen gas. Tribol Int 157: 106884 (2021)
DOI Google Scholar
[11]
Johansson P, Marklund P, Björling M, Shi Y J. Effect of humidity and counterface material on the friction and wear of carbon fiber reinforced PTFE composites. Tribol Int 157: 106869 (2021)
DOI Google Scholar
[12]
Johansson P, Marklund P, Björling M, Shi Y J. Effect of roughness on the running-in behavior and tribofilm formation of carbon fiber reinforced PTFE composite in trace moisture environment. Wear 500–501: 204367 (2022)
DOI Google Scholar
[13]
Kojima H, Sawae Y, Morita T, Sugimura J. Effect of trace moisture content on friction of carbon fiber filled PTFE in high purity gas. In: Proceedings of the Malaysian International Tribology Conference, 2015: 125–126.
DOI Google Scholar
[14]
Abe Y, Kojima H, Morita T, Onitsuka S, Sawae Y, Sugimura J. Effects of trace moisture content on friction and wear of carbon fiber filled PTFE in hydrogen. Proc Mech Eng Congr Jpn 2016: S1160106 (2016)
DOI Google Scholar
[15]
Schubert R. The influence of a gas atmosphere and its moisture on sliding wear in PTFE compositions. J Lubr Technol 93(2): 216–223 (1971)
DOI Google Scholar
[16]
Theiler G, Gradt T. Environmental effects on the sliding behaviour of PEEK composites. Wear 368–369: 278–286 (2016)
DOI Google Scholar
[17]
Oyamada T, Ono M, Miura H, Kuwano T. Effect of gas environment on friction behavior and tribofilm formation of PEEK/carbon fiber composite. Tribol Trans 56(4): 607–614 (2013)
DOI Google Scholar
[18]
Brubaker Z E, Langford J J, Kapsimalis R J, Niedziela J L. Quantitative analysis of Raman spectral parameters for carbon fibers: Practical considerations and connection to mechanical properties. J Mater Sci 56(27): 15087–15121 (2021)
DOI Google Scholar
[19]
Johansson P, Elo R, Naeini V F, Marklund P, Björling M, Shi Y J. Insights of the ultralow wear and low friction of carbon fiber reinforced PTFE in inert trace moisture environment. Tribol Lett 71(3): 1–18 (2023)
DOI Google Scholar
[20]
Han B, Kim D S. Moisture ingress, behavior, and prediction inside semiconductor packaging: A review. J Electron Packag 139(1): 010802 (2017)
DOI Google Scholar
[21]
Johansson P, Kalliorinne K, Marklund P, Björling M. Precise control of operating conditions in tribotesting with respect to trace humidity and contact temperature. MethodsX 8: 101362 (2021)
DOI Google Scholar
[22]
Haidar D R, Alam K I, Burris D L. Tribological insensitivity of an ultralow-wear poly(etheretherketone)–polytetrafluoroethylene polymer blend to changes in environmental moisture. J Phys Chem C 122(10): 5518–5524 (2018)
DOI Google Scholar
[23]
McCook N L, Hamilton M A, Burris D L, Sawyer W G. Tribological results of PEEK nanocomposites in dry sliding against 440C in various gas environments. Wear 262(11–12): 1511–1515 (2007)
DOI Google Scholar
[24]
Zaïdi H, Néry H, Paulmier D. Stability of lubricating properties of graphite by orientation of the crystallites in the presence of water vapour. Appl Surf Sci 70–71: 180–185 (1993)
DOI Google Scholar
[25]
Zaidi H, Paulmier D, Jeanmaire A, Nery H. Behaviour of graphite in friction under various environments. Surf Sci 251–252: 778–781 (1991)
DOI Google Scholar
[26]
Khedkar J, Negulescu I, Meletis E I. Sliding wear behavior of PTFE composites. Wear 252(5–6): 361–369 (2002)
DOI Google Scholar
[27]
Unal H, Yetgin S H, Mimaroglu A, Sumer M. The effect of test parameters on friction and wear performance of PTFE and PTFE composites. J Reinf Plast Compos 29(13): 1978–1986 (2010)
DOI Google Scholar
[28]
Ullah S, Haque F M, Sidebottom M A. Maintaining low friction coefficient and ultralow wear in metal-filled PTFE composites. Wear 498–499: 204338 (2022)
DOI Google Scholar
[29]
Khare H S, Moore A C, Haidar D R, Gong L, Ye J, Rabolt J F, Burris D L. Interrelated effects of temperature and environment on wear and tribochemistry of an ultralow wear PTFE composite. J Phys Chem C 119(29): 16518–16527 (2015)
DOI Google Scholar
[30]
Sun W, Liu X J, Liu K, Xu J M, Lu Y X, Ye J X. Mechanochemical functionality of graphene additives in ultralow wear polytetrafluoroethylene composites. Carbon 184: 312–321 (2021)
DOI Google Scholar
[31]
Blower P J, Levason W, Luthra S K, McRobbie G, Monzittu F M, Mules T O, Reid G, Subhan M N. Exploring transition metal fluoride chelates—-Synthesis, properties and prospects towards potential PET probes. Dalton Trans 48(20): 6767–6776 (2019)
DOI Google Scholar
[32]
Nyquist R A, Kagel R O. Handbook of Infrared and Raman Spectra of Inorganic Compounds and Organic Salts: Infrared Spectra of Inorganic Compounds. Elsevier Inc., 1971.
DOI
[33]
Togashi T, Naka T, Asahina S, Sato K, Takami S, Adschiri T. Surfactant-assisted one-pot synthesis of superparamagnetic magnetite nanoparticle clusters with tunable cluster size and magnetic field sensitivity. Dalton Trans 40(5): 1073–1078 (2011)
DOI Google Scholar
[34]
Pitenis A A, Harris K L, Junk C P, Blackman G S, Sawyer W G, Krick B A. Ultralow wear PTFE and alumina composites: It is all about tribochemistry. Tribol Lett 57(1): 1–8 (2015)
DOI Google Scholar
[35]
Qi H M, Zhang G, Chang L, Zhao F Y, Wang T M, Wang Q H. Ultralow friction and wear of polymer composites under extreme unlubricated sliding conditions. Adv Materials Inter 4(13): 1601171 (2017)
DOI Google Scholar
[36]
Bhargava S, Makowiec M E, Blanchet T A. Wear reduction mechanisms within highly wear-resistant graphene- and other carbon-filled PTFE nanocomposites. Wear 444–445: 203163 (2020)
DOI Google Scholar
[37]
Sidebottom M, Pitenis A, Junk C, Kasprzak D J, Blackman G, Burch H E, Harris K L, Sawyer W, Krick B. Ultralow wear Perfluoroalkoxy (PFA) and alumina composites. Wear 362: 179–185 (2016)
DOI Google Scholar
[38]
Krick B A, Pitenis A A, Harris K L, Junk C P, Sawyer W G, Brown S C, Rosenfeld H D, Kasprzak D J, Johnson R S, Chan C D, et al. Ultralow wear fluoropolymer composites: Nanoscale functionality from microscale fillers. Tribol Int 95: 245–255 (2016)
DOI Google Scholar
[39]
Sun W, Liu X J, Liu K, Zhang Y, Lu Y X, Ye J X. (2022) Suppression of wear in gallium nitride fibers reinforced fluoropolymer composites: Synergistic effects of load support and tribochemistry. Tribology International 165: 107286 (2022)
DOI Google Scholar
[40]
Alam K, Burris D. Ultralow wear poly(tetrafluoroethylene): A virtuous cycle of wear reduction and tribochemical accumulation. The Journal of Physical Chemistry C 125(35): 19417–19427 (2021)
DOI Google Scholar
[41]
Otero V, Sanches D, Montagner C, Vilarigues M, Carlyle L, Lopes J A, Melo M J. Characterisation of metal carboxylates by Raman and infrared spectroscopy in works of art. J Raman Spectrosc 45(11–12): 1197–1206 (2014)
DOI Google Scholar
[42]
Gao X D, Chorover J. Adsorption of perfluorooctanoic acid and perfluorooctanesulfonic acid to iron oxide surfaces as studied by flow-through ATR-FTIR spectroscopy. Environ Chem 9(2): 148 (2012)
DOI Google Scholar
[43]
Crowell J E, Chen J G, Yates J T Jr. A vibrational study of the adsorption and decomposition of formic acid and surface formate on Al(111). J Chem Phys 85(5): 3111–3122 (1986)
DOI Google Scholar
[44]
Lu Y Q, Miller J D. Carboxyl stretching vibrations of spontaneously adsorbed and LB-transferred calcium carboxylates as determined by FTIR internal reflection spectroscopy. J Colloid Interface Sci 256(1): 41–52 (2002)
DOI Google Scholar
[45]
Palacios E G, Juárez-López G, Monhemius A J. Infrared spectroscopy of metal carboxylates. Hydrometallurgy 72(1–2): 139–148 (2004)
DOI Google Scholar
[46]
Oshima A, Tanaka T, Nakaya H, Senba R, Satoh K. Pentadecafluorooctanoic-acid-free polytetrafluoroethylene and mechanism of PFOA formation by γ-irradiation. Sci Rep 10(1): 13940 (2020)
DOI Google Scholar
[47]
Sha F X, Cheng G J, Xuan Z Y, Liu Y, Liu W H, Zhang X D, Tang Z F. Free-radical evolution and decay in cross-linked polytetrafluoroethylene irradiated by gamma-rays. Nucl Sci Tech 33(5): 1–13 (2022)
DOI Google Scholar
[48]
Harris K L, Pitenis A A, Sawyer W G, Krick B A, Blackman G S, Kasprzak D J, Junk C P. PTFE tribology and the role of mechanochemistry in the development of protective surface films. Macromolecules 48(11): 3739–3745 (2015)
DOI Google Scholar
[49]
Jayarathna L, Bandara A, Ng W J, Weerasooriya R. Fluoride adsorption on γ-Fe2O3 nanoparticles. J Environ Health Sci Eng 13: 54 (2015)
DOI Google Scholar
[50]
Kartick B, Srivastava S K, Srivastava A I. Green synthesis of graphene. J Nanosci Nanotechnol 13(6): 4320–4324 (2013)
DOI Google Scholar
[51]
Rochman R A, Wahyuningsih S, Ramelan A H, Hanif Q A. Preparation of nitrogen and sulphur Co-doped reduced graphene oxide (rGO-NS) using N and S heteroatom of thiourea. IOP Conf Ser: Mater Sci Eng 509: 012119 (2019)
DOI Google Scholar
[52]
Marcano D C, Kosynkin D V, Berlin J M, Sinitskii A, Sun Z Z, Slesarev A, Alemany L B, Lu W, Tour J M. Improved synthesis of graphene oxide. ACS Nano 4(8): 4806–4814 (2010)
DOI Google Scholar
[53]
Leal D, Matsuhiro B, Rossi M, Caruso F. FT-IR spectra of alginic acid block fractions in three species of brown seaweeds. Carbohydr Res 343(2): 308–316 (2008)
DOI Google Scholar
[54]
Morstein C E, Klemenz A, Dienwiebel M, Moseler M. Humidity-dependent lubrication of highly loaded contacts by graphite and a structural transition to turbostratic carbon. Nat Commun 13(1): 5958 (2022)
DOI Google Scholar
[55]
Yen B K. Influence of water vapor and oxygen on the tribology of carbon materials with sp2 valence configuration. Wear 192(1–2): 208–215 (1996)
DOI Google Scholar
[56]
Yen B K, Schwickert B E, Toney M F. Origin of low-friction behavior in graphite investigated by surface X-ray diffraction. Appl Phys Lett 84(23): 4702–4704 (2004)
DOI Google Scholar
[57]
Lin Z B, Zhang K, Ye J X, Li X J, Zhao X G, Qu T, Liu Q F, Gao B Z. The effects of filler type on the friction and wear performance of PEEK and PTFE composites under hybrid wear conditions. Wear 490–491: 204178 (2022)
DOI Google Scholar
[58]
Campbell K L, Sidebottom M A, Atkinson C C, Babuska T F, Kolanovic C A, Boulden B J, Junk C P, Krick B A. Ultralow wear PTFE-based polymer composites—The role of water and tribochemistry. Macromolecules 52(14): 5268–5277 (2019)
DOI Google Scholar
[59]
Alam K I, Dorazio A, Burris D L. Polymers tribology exposed: Eliminating transfer film effects to clarify ultralow wear of PTFE. Tribol Lett 68(2): 1–13 (2020)
DOI Google Scholar
[60]
Zuo Z, Yang Y L, Qi X W, Su W W, Yang X C. Analysis of the chemical composition of the PTFE transfer film produced by sliding against Q235 carbon steel. Wear 320: 87–93 (2014)
DOI Google Scholar
[61]
Gao J T. Tribochemical effects in formation of polymer transfer film. Wear 245(1–2): 100–106 (2000)
DOI Google Scholar
[62]
Sun W, Liu X J, Song Q R, Liu K, Wang W, Lu Y X, Ye J X. Mechanochemical effect of filler surface functionality on fluoropolymer tribology. Macromolecules 54(13): 6417–6429 (2021)
DOI Google Scholar
[63]
Restuccia P, Ferrario M, Righi M C. Monitoring water and oxygen splitting at graphene edges and folds: Insights into the lubricity of graphitic materials. Carbon 156: 93–103 (2020)
DOI Google Scholar
[64]
Rietsch J C, Brender P, Dentzer J, Gadiou R, Vidal L, Vix-Guterl C. Evidence of water chemisorption during graphite friction under moist conditions. Carbon 55: 90–97 (2013)
DOI Google Scholar
[65]
Hontoria-Lucas C, López-Peinado A J, de D López-González J, Rojas-Cervantes M L, Martín-Aranda R M. Study of oxygen-containing groups in a series of graphite oxides: Physical and chemical characterization. Carbon 33(11): 1585–1592 (1995)
DOI Google Scholar
[66]
Hiratsuka K, Mariko R, Tsutsumi T. Effects of sliding speed, periodic pauses, and atmospheric moisture content on the wear of graphite against cast iron. Wear 424–425: 255–260 (2019)
DOI Google Scholar
Publication history
Copyright
Rights and permissions

Publication history

Received: 05 July 2023
Revised: 26 August 2023
Accepted: 05 September 2023
Published: 04 December 2023
Issue date: May 2024

Copyright

© The author(s) 2023.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.

The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.

To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Return