Journal Home > Volume 2 , Issue 4

The CaO–P2O5–SiO2–MgO system presents several compounds used as biomaterials such as hydroxyapatite (HA), tricalcium phosphate (TCP) and TCP with magnesium substituting partial calcium (TCMP). The β-TCMP phase with whitlockite structure has interesting biological features and mechanical properties, meeting the requirements of a bioactive material for bone restoration. In this work, the production of Mg-doped TCP, β-TCMP, has been investigated by crystallization from a glass composed of 52.75 wt% 3CaO·P2O5, 30 wt% SiO2 and 17.25 wt% MgO (i.e., 31.7 mol% CaO, 10.6 mol% P2O5, 26.6 mol% MgO and 31.1 mol% SiO2) using heat treatments between 775 ℃ and 1100 ℃ for up to 8 h. The devitrification process of the glass has been accompanied by differential scanning calorimetry (DSC), high-resolution X-ray diffraction (HRXRD), relative density and bending strength measurements. The characterization by HRXRD and DSC revealed the occurrence of whitlockite soon after the bulk glass preparation, a transient non-cataloged silicate between 800 ℃ and 1100 ℃, and the formation of diopside in samples treated at 1100 ℃ as crystalline phases. The overall crystalline fraction varied from 26% to 70% depending on the heat treatments. Furthermore, contraction of the a-axis lattice parameter and expansion of the c-axis lattice parameter of the whitlockite structure have been observed during the heat treatments, which were attributed to the β-TCMP formation with the partial substitution of Ca2+ by Mg2+. Relative densities near 99% and 97% for the glass and glass-ceramics respectively indicated a discrete reduction as a function of the devitrification treatment. Bending strengths of 70 MPa and 120 MPa were determined for the glass and glass-ceramic material crystallized at 975 ℃ for 4 h, respectively.


menu
Abstract
Full text
Outline
About this article

Development and characterization of 3CaO·P2O5–SiO2–MgO glass-ceramics with different crystallization degree

Show Author's information Juliana Kelmy M. F. DAGUANOaPaulo A. SUZUKIaKurt STRECKERbJosé Martinho Marques de OLIVEIRAcMaria Helena Figueira Vaz FERNANDESdClaudinei SANTOSa,e,*( )
Universidade de São Paulo - Escola de Engenharia de Lorena, USP-EEL - Pólo Urbo-Industrial, s/n, Gleba AI-6, Lorena-SP, CEP 12600-000, Brazil
Universidade Federal de São João del-Rei, – UFSJ-CENEN, Campus Sto Antônio - Praça Frei Orlando 170 – Centro, S. J. del-Rei-MG. CEP 36307-352, Brazil
Escola Superior Aveiro Norte, Edifício Rainha, 3720-232 O. Azeméis, Portugal
Universidade de Aveiro, Campus Universitário de Santiago3810-193 Aveiro, Portugal
Universidade do Estado do Rio de Janeiro – Faculdade de Tecnologia de Resende – UERJ-FAT – Rod. Presidente Dutra, km, 298, Resende-RJ, CEP 27537-000, Brazil

Abstract

The CaO–P2O5–SiO2–MgO system presents several compounds used as biomaterials such as hydroxyapatite (HA), tricalcium phosphate (TCP) and TCP with magnesium substituting partial calcium (TCMP). The β-TCMP phase with whitlockite structure has interesting biological features and mechanical properties, meeting the requirements of a bioactive material for bone restoration. In this work, the production of Mg-doped TCP, β-TCMP, has been investigated by crystallization from a glass composed of 52.75 wt% 3CaO·P2O5, 30 wt% SiO2 and 17.25 wt% MgO (i.e., 31.7 mol% CaO, 10.6 mol% P2O5, 26.6 mol% MgO and 31.1 mol% SiO2) using heat treatments between 775 ℃ and 1100 ℃ for up to 8 h. The devitrification process of the glass has been accompanied by differential scanning calorimetry (DSC), high-resolution X-ray diffraction (HRXRD), relative density and bending strength measurements. The characterization by HRXRD and DSC revealed the occurrence of whitlockite soon after the bulk glass preparation, a transient non-cataloged silicate between 800 ℃ and 1100 ℃, and the formation of diopside in samples treated at 1100 ℃ as crystalline phases. The overall crystalline fraction varied from 26% to 70% depending on the heat treatments. Furthermore, contraction of the a-axis lattice parameter and expansion of the c-axis lattice parameter of the whitlockite structure have been observed during the heat treatments, which were attributed to the β-TCMP formation with the partial substitution of Ca2+ by Mg2+. Relative densities near 99% and 97% for the glass and glass-ceramics respectively indicated a discrete reduction as a function of the devitrification treatment. Bending strengths of 70 MPa and 120 MPa were determined for the glass and glass-ceramic material crystallized at 975 ℃ for 4 h, respectively.

Keywords: glass-ceramics, heat treatment, high-resolution X-ray diffraction (HRXRD), bending strength

References(23)

[1]
LeGeros RZ. Properties of osteoconductive biomaterials: Calcium phosphates. Clin Orthop Relat Res 2002, 395: 81-98.
[2]
Park JB, Lakes RS. Ceramic implant materials. In Biomaterials: An Introduction, 3rd edn. New York: Springer, 2007: 139-171.
[3]
Rodrigues CVM, Serricella P, Linhares ABR, et al. Characterization of a bovine collagen–hydroxyapatite composite scaffold for bone tissue engineering. Biomaterials 2003, 24: 4987-4997.
[4]
Billotte WG. Ceramic biomaterials. In Biomaterials: Principles and Applications. Park JB, Bronzino JD, Eds. Boca Raton: CRC Press, 2003: 21-54.
DOI
[5]
Elliot JC. Structure and Chemistry of the Apatites and Other Calcium Orthophosphates, 2nd end. Vol.18 Studies in Inorganic Chemistry. Elsevier Science & Technology, 1994.
[6]
Ribeiro GBM, Trommer RM, dos Santos LA, et al. Novel method to produce β-TCP scaffolds. Mater Lett 2011, 65: 275-277.
[7]
Bigi A, Cojazzi G, Panzavolta S, et al. Chemical and structural characterization of the mineral phase from cortical and trabecular bone. J Inorg Biochem 1997, 68: 45-51.
[8]
Kannan S, Ventura JM, Ferreira JMF. Aqueous precipitation method for the formation of Mg-stabilized β-tricalcium phosphate: An X-ray diffraction study. Ceram Int 2007, 33: 637-641.
[9]
Araújo JC, Sader MS, Moreira EL, et al. Maximum substitution of magnesium for calcium sites in Mg-β-TCP structure determined by X-ray powder diffraction with the Rietveld refinement. Mater Chem Phys 2009, 118: 337-340.
[10]
Daguano JKMF, Santos C, Suzuki PA, et al. Improvement of the mechanical properties of glasses based on the 3CaO·P2O5–SiO2–MgO system after heat-treatment. Mater Sci Forum 2010, 636–637: 41-46.
[11]
Bose S, Tarafder S, Banerjee SS, et al. Understanding in vivo response and mechanical property variation in MgO, SrO and SiO2 doped β-TCP. Bone 2011, 48: 1282-1290.
[12]
Banerjee SS, Tarafder S, Davies NM, et al. Understanding the influence of MgO and SrO binary doping on the mechanical and biological properties of β-TCP ceramics. Acta Biomater 2010, 6: 4167-4174.
[13]
Schroeder LW, Dickens B, Brown WE. Crystallographic studies of the role of Mg as a stabilizing impurity in β-Ca3(PO4)2. II. Refinement of Mg-containing β-Ca3(PO4)2. J Solid State Chem 1977, 22: 253-262.
[14]
Enderle R, Götz-Neurnhoeffer F, Göbbels M, et al. Influence of magnesium doping on the phase transformation temperature of β-TCP ceramics examined by Rietveld refinement. Biomaterials 2005, 26: 3379-3384.
[15]
Oliveira AL, Oliveira JM, Correia RN, et al. Crystallization of Whitlockite from a glass in the system CaOP2O5SiO2MgO. J Am Ceram Soc 1998, 81: 3270-3276.
[16]
Oliveira JM, Correia RN, Fernandes MH. Surface modifications of a glass and a glass-ceramic of the MgO–3CaO·P2O5–SiO2 system in a simulated body fluid. Biomaterials 1995, 16: 849-854.
[17]
Krimm S, Tobolsky AV. Quantitative X-ray studies of order in amorphous and crystalline polymers. Quantitative X-ray determination of crystallinity in polyethylene. J Polym Sci 1951, 7: 57-76.
[18]
Ray CS, Yang Q, Huang W, et al. Surface and internal crystallization in glasses as determined by differential thermal analysis. J Am Ceram Soc 1996, 79: 3155-3160.
[19]
Oliveira AL, Oliveira JM, Correia RN, et al. Phase separation and crystallization in 3CaO·P2O5–SiO2–MgO glasses. In Proceedings of the 5th International Otto Schott Colloquium. Vol.67 Glass Science and Technology. Dt. Glastechn. Ges., 1994: 367-370.
[20]
Queiroz CMGA. Cristalização de biomateriais vitrocerâmicos e mineralização em meio fisiológico simulado. Doctoral Thesis. Portugal: Universidade de Aveiro, 2005.
[21]
Holand W, Beall GH. Glass-Ceramic Technology. New York: Wiley-Blackwell, 2002.
[22]
Karamanov A, Pelino M. Induced crystallization porosity and properties of sintereds diopside and wollastonite glass-ceramics. J Eur Ceram Soc 2008, 28: 555-562.
[23]
Karamanov A, Pelino M. Sinter-crystallisation in the diopside–albite system: Part I. Formation of induced crystallisation porosity. J Eur Ceram Soc 2006, 26: 2511-2517.
Publication history
Copyright
Acknowledgements
Rights and permissions

Publication history

Received: 09 September 2013
Revised: 23 October 2013
Accepted: 30 October 2013
Published: 04 December 2013
Issue date: December 2013

Copyright

© The author(s) 2013

Acknowledgements

The authors would like to thank LNLS - Laboratório Nacional de Luz Síncrotron for technical support, and FAPESP for financial support, under grant No. 07/50510-4. We also acknowledge Prof. E. D. Zanotto and the LaMaV, UFSCar, for melting of glass and DSC analysis.

Rights and permissions

Open Access: This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution, and reproduction in any medium, provided the original author(s) and the source are credited.

Return