Journal Home > Volume 9 , Issue 4

Conducting polymers generally show high specific capacitance but suffer from poor rate capability and rapid capacitance decay, which greatly limits their practical applications in supercapacitor electrodes. To this end, many studies have focused on improving the overall capacitive performance by synthesizing nanostructured conducting polymers or by depositing a range of coatings to increase the active surface area exposed to the electrolyte and enhance the charge transport efficiency and structural stability. Despite this, simultaneously achieving high specific capacitance, good rate performance, and long cycle life remains a considerable challenge. Among the various two-dimensional (2D) layered materials, octahedral (1T) phase molybdenum disulfide (MoS2) nanosheets have high electrical conductivity, large specific surface areas, and unique surface chemical characteristics, making them an interesting substrate for the controlled growth of nanostructured conducting polymers. This paper reports the rational synthesis of carbon shell-coated polyaniline (PANI) grown on 1T MoS2 monolayers (MoS2/PANI@C). The composite electrode comprised of MoS2/PANI@C with a ~3 nm carbon shell exhibited a remarkable specific capacitance of up to 678 F·g–1 (1 mV·s–1), superior capacity retention of 80% after 10, 000 cycles and good rate performance (81% at 10 mV·s–1) due to the multiple synergic effects between the PANI nanostructure and 1T MoS2 substrates as well as protection by the uniform thin carbon shell. These properties are comparable to the best overall capacitive performance achieved for conducting polymers-based supercapacitor electrodes reported thus far.

File
nr-9-4-951_ESM.pdf (4.3 MB)
Publication history
Copyright
Acknowledgements

Publication history

Received: 08 November 2015
Revised: 16 December 2015
Accepted: 18 December 2015
Published: 01 February 2016
Issue date: April 2016

Copyright

© Tsinghua University Press and Springer-Verlag Berlin Heidelberg 2016

Acknowledgements

Acknowledgements

We are grateful for financial support from Fudan University, National Basic Research Program of China (No. 2011CB605702), National Natural Science Foundation of China (No. 51173027), The Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning (No. TP2015002) and Shanghai Basic Research Program (No. 14JC1400600). We also thank Miss Q. Yan, Dr. L. Dei, Dr. G. Qi, Dr. Y. Cui and Dr. Y. Ren at Fudan University and Miss Q. Hu at Shanghai Jiao Tong University for the help with the experiments. Dr. S. Ye and Dr. Y. Zhang at Fudan University provide some suggestions, too. I. S. would like to extend his sincere appreciation to the Deanship of Scientific Research at the King Saud University for its funding of this research through the Research Prolific Research Group, Project No PRG-1436-25.

Return