The addition of Au3+ to spherical amine-capped CdSe@ZnS nanoparticles in toluene at room temperature and under darkness can lead to ternary CdSe@ZnS/Au nanohybrids. We demonstrate that this happens only when the nanoparticles possess a relatively thin ZnS shell, thus showing that thickness plays a key role in gold deposition on the CdSe@ZnS nanoparticle surface. Our hypothesis is that the amine ligand acts as the reductant of Au3+ ions into Au+ ions, whose affinity for sulfur would keep them at the CdSe@ZnS surface. This interaction stabilizes the Au+ ion, making it less prone to reduction than a non-coordinated Au+ ion. In CdSe@ZnS with a thin shell, Au+ ions at the surface of, or most probably within, the ZnS shell cause the transfer of Cd2+ ions into the solution. Subsequently, the core Se2– anion, which is a better reductant than the shell S2–, reduces Au+ ions to Au(0), and large gold nanoparticles (AuNPs) are quickly deposited on the CdSe@ZnS surface in room temperature process, leading to ternary CdSe@ZnS/Au nanohybrids. In solution, these ternary nanohybrids progressively transform into quaternary CdSe@ZnS/Au2S/Au nanohybrids due to the reaction of the shell S2– anion with the remaining Au+ at the CdSe@ZnS surface, thus leading to the growth of Au2S nanoparticles on the CdSe@ZnS surface while Zn concomitantly leaches from the nanohybrid into the solution. Photoirradiation of the heterostructures with visible light enhances their emission efficiency. Comparatively, irradiation of the precursors, i.e., CdSe@ZnS nanoparticles, causes a drastic decrease in their emission accompanied by a blue shift of their emission maximum. The optical properties of these nanohybrids were analyzed by absorption and fluorescence (steady-state and time-resolved) spectroscopy, and the composition of the samples and the chemical states were determined by energy dispersive X-ray spectroscopy (EDX) and X-ray photoelectron spectroscopy (XPS), respectively. Finally, the structural and morphological characterizations of the nanohybrids were performed by bright-field transmission electron microscopy (TEM), dark-field TEM, high-resolution TEM (HRTEM), and selected-area electron diffraction (SAED).

File
12274_2015_738_MOESM1_ESM.pdf (5.1 MB)
Publication history
Copyright
Acknowledgements

Publication history

Received: 07 October 2014
Revised: 27 January 2015
Accepted: 28 January 2015
Published: 09 May 2015
Issue date: July 2015

Copyright

© Tsinghua University Press and Springer-Verlag Berlin Heidelberg 2015

Acknowledgements

Acknowledgements

We thank the Spanish Ministry of Economy and Competitiveness (MINECO Project CTQ2011-27758, CTQ2011-26507), and FGUV (R. E. G.) for financial support. The authors are also grateful to the Central Support Service in Experimental Research (SCSIE), University of Valencia, Spain for providing TEM facility.

Return