TY - JOUR AU - XIONG, Yao AU - TANG, Zilong AU - WANG, Yu AU - HU, Yongming AU - GU, Haoshuang AU - LI, Yuanzhi AU - CHAN, Helen Lai Wah AU - CHEN, Wanping PY - 2015 TI - Gas sensing capabilities of TiO2 porous nanoceramics prepared through premature sintering JO - Journal of Advanced Ceramics SN - 2226-4108 SP - 152 EP - 157 VL - 4 IS - 2 AB - Pure and noble metal (Pt, Pd, and Au) doped TiO2 nanoceramics have been prepared from TiO2 nanoparticles through traditional pressing and sintering. For those samples sintered at 550 ℃, a typical premature sintering occurred, which led to the formation of a highly porous microstructure with a Brunauer–Emmett–Teller (BET) specific surface area of 23 m2/g. At room temperature, only Pt-doped samples showed obvious response to hydrogen, with sensitivities as high as ~500 for 1000 ppm H2 in N2; at 300 ℃, all samples showed obvious responses to CO, while the responses of noble metal doped samples were much higher than that of the undoped ones. The mechanism for the observed sensing capabilities has been discussed, in which the catalytic effect of Pt for hydrogen is believed responsible for the room-temperature hydrogen sensing capabilities, and the absence of glass frit as commonly used in commercial thick-film metal oxide gas sensors is related to the high sensitivities. It is proposed that much attention should be paid to metal oxide porous nanoceramics in developing gas sensors with high sensitivities and low working temperatures. UR - https://doi.org/10.1007/s40145-015-0148-y DO - 10.1007/s40145-015-0148-y