title = {Mechanisms of Pore-Grain Boundary Interactions Influencing Nanoindentation Behavior in Pure Nickel: A Molecular Dynamics Study},
year = {2026},
journal = {Computers, Materials & Continua},
volume = {86},
number = {1},
pages = {1-21},
keywords = {Pure nickel, nanoindentation, molecular dynamics, pore, grain boundary},
url = {https://www.sciopen.com/article/10.32604/cmc.2025.068655},
doi = {10.32604/cmc.2025.068655},
abstract = {THE mechanical response and deformation mechanisms of pure nickel under nanoindentation were systematically investigated using molecular dynamics (MD) simulations, with a particular focus on the novel interplay between crystallographic orientation, grain boundary (GB) proximity, and pore characteristics (size/location). This study compares single-crystal nickel models along [100], [110], and [111] orientations with equiaxed polycrystalline models containing 0, 1, and 2.5 nm pores in surface and subsurface configurations. Our results reveal that crystallographic anisotropy manifests as a 24.4% higher elastic modulus and 22.2% greater hardness in [111]-oriented single crystals compared to [100]. Pore-GB synergistic effects are found to dominate the deformation behavior: 2.5 nm subsurface pores reduce hardness by 25.2% through stress concentration and dislocation annihilation at GBs, whereas surface pores enable mechanical recovery via accelerated dislocation generation post-collapse. Additionally, size-dependent deformation regimes were identified, with 1 nm pores inducing negligible perturbation due to rapid atomic rearrangement, in contrast with persistent softening in 2.5 nm pores. These findings establish atomic-scale design principles for defect engineering in nickel-based aerospace components, demonstrating how crystallographic orientation, pore configuration, and GB interactions collectively govern nanoindentation behavior.}
}