author = {Wanpeng YANG and Jiarong LI and Jinqian ZHAO and Jian YU and Xiaoguang WANG and Shizhong LIU and Qiao CHEN},
title = {Effects of low angle boundaries on tensile behaviors of a third generation single crystal superalloy at 760-980 ℃},
year = {2026},
journal = {Journal of Aeronautical Materials},
volume = {46},
number = {8},
pages = {58-65},
keywords = {third generation single crystal superalloy, low angle boundaries, tensile property, fracture mechanism},
url = {https://www.sciopen.com/article/10.11868/j.issn.1005-5053.2026.000105},
doi = {10.11868/j.issn.1005-5053.2026.000105},
abstract = {The influence of low angle boundaries (LABs) on the tensile behavior of a third generation single crystal superalloy at temperatures of 760, 850 ℃, and 980 ℃ has been explored. The microstructure of the specimens after tensile rupture is examined using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The findings reveal that the third generation single crystal superalloy with LABs demonstrates favorable tensile properties. LABs with angles ranging from 0° to 8.9° have a negligible impact on the yield strength and ultimate tensile strength of the alloy at 760, 850 ℃, and 980 ℃. At 980 ℃, the tensile strength of the specimen with LABs of 11.4° decreases by 80 MPa compared to that of the specimen with LABs of 0°. As the angle of the LABs increases, the elongation of the alloy with LABs in the range of 0°-11.4° at 980 ℃ exhibits a downward trend. Additionally, the propensity for intergranular fracture in the alloy with LABs becomes more pronounced as either the angle of the LABs increases or the temperature rises.}
}