@article{Wang2026, 
author = {Boran Wang and Zhongyan Wang and Xin Li and Yu Chen and Rui Ge and Yongkang Yang and Jiachen Liu and Anran Guo},
title = {Achieving superior thermal stability in vat photopolymerized silica-based ceramic cores via kyanite-induced expansion compensation},
year = {2026},
journal = {Journal of Advanced Ceramics},
volume = {15},
number = {6},
pages = {9221313},
keywords = {ceramic cores, vat photopolymerization (VPP), shrinkage compensation, thermal expansion, creep resistance, comprehensive performance evaluation},
url = {https://www.sciopen.com/article/10.26599/JAC.2026.9221313},
doi = {10.26599/JAC.2026.9221313},
abstract = {Vat photopolymerization (VPP) three-dimensional (3D) printing has emerged as a predominant technology for fabricating complex-shaped ceramic cores used in aeroengine hollow turbine blades. However, the inherent limitations of VPP 3D printing-fabricated silica-based cores, such as excessive sintering shrinkage and high-temperature deflection, have severely restricted their application in high-performance investment casting. In this study, we proposed a novel strategy to overcome this challenge by introducing kyanite into the silica-based ceramic core. The influence of kyanite content on microstructural evolution and comprehensive properties was systematically explored, and a ceramic core quality index (CQI) model was further established to evaluate the comprehensive performance. The results indicated that when the kyanite content exceeded 15 wt%, the volume expansion resulting from high-temperature decomposition effectively inhibited sintering shrinkage within the temperature range of 1300–1400 °C. Furthermore, the columnar mullite crystals generated from decomposition acted as the key factor enhancing the high-temperature performance. Optimal comprehensive properties, corresponding to a maximum CQI score of 78.85, were achieved with a kyanite content of 15 wt% and a sintering temperature of 1225 °C. Under this condition, the sintering shrinkage and casting shrinkage of ceramic cores were reduced to 3.06% and 0.86%, respectively. Additionally, the high-temperature deflection was significantly decreased to 0.82 mm, while the flexural strength and high-temperature flexural strength reached 10.06 and 27.05 MPa, respectively. This study provides a novel strategy for fabricating silica-based ceramic cores with lower sintering and casting shrinkage while elucidating the regulatory mechanism of kyanite on the core properties.}
}