@article{Peng2023, 
author = {Rui Peng and Yongcheng Lu and Liang Shi and Guoliang Yu and Yuanming Lai and Gang Wang and Yuanxun Li and Hua Su and Huaiwu Zhang},
title = {High sintering and dielectric performance: The improved (Mg, Zn)3B2O6 ceramics with the help of the DFT calculation},
year = {2023},
journal = {Journal of Magnesium and Alloys},
volume = {11},
number = {6},
pages = {2142-2150},
keywords = {DFT, Borate, Solid solutions, Dielectric properties},
url = {https://www.sciopen.com/article/10.1016/j.jma.2021.08.033},
doi = {10.1016/j.jma.2021.08.033},
abstract = {With the help of the first principle calculation, the solid-state reaction experiment was conducted to investigate the alteration in the sintering and the microwave dielectric properties of Mg3B2O6 ceramic with many Zn2+ substitutions. These properties were characterized using the scanning electron microscopy, network analyzer, X-ray diffraction, Raman spectroscopy, energy-dispersive spectroscopy, and thermomechanical and differential-thermal analyses. The coexistence of Mg3B2O6, Mg2B2O5 and ZnO ceramics could be observed with increasing Zn2+ addition, and the lattice distortion occurred in the Mg2B2O5 and Mg3B2O6 ceramics due to the substitution of Mg2+ with Zn2+. The electron density and the bond property of the MgO6 octahedron changed, and a quantitative method was used to discuss the variation in sintering, substitution and phase formation properties. The densification window was decreased to 1100 °C, and the dielectric properties improved with the formation of a three-phase borate solid solution (dielectric constant = 6.73, quality factor = 112,000 GHz at 16 GHz (Q = 7000), temperature coefficient of resonant frequency = −61.2 ppm °C−1, and relative density = 97.0%).}
}