@article{CHEN2022, 
author = {Wei CHEN and ChaoLong ZHU and Xin JIA and ZiQiang ZHAO and XiuQing LI},
title = {Microstructure and Physical and Mechanical Properties of Si3N4/Ni Composite with Tree-Ring Imitating Structure},
year = {2022},
journal = {Journal of the Chinese Ceramic Society},
volume = {50},
number = {6},
pages = {1548-1556},
keywords = {silicon nitride/nickel composite, wood tree ring-like, toughening, microstructure, interface, mechanical properties},
url = {https://www.sciopen.com/article/10.14062/j.issn.0454-5648.20210774},
doi = {10.14062/j.issn.0454-5648.20210774},
abstract = {Although engineering ceramics are widely used in industry, its high brittleness is one of the main factors restricting its popularization. This paper was to synergistically improve the strength and toughness of engineering structural ceramics. A wood tree ring-like Si3N4/Ni composite was prepared with micron-sized powder of Si3N4 and high purity nickel wire via hot pressing sintering. The interface bonding between Si3N4 matrix and Ni wire in Si3N4/Ni composite was investigated, and the physical and mechanical properties of the composite were characterized. The results show that the interface between Si3N4 matrix and Ni wire in the composite is well bonded, and the wood tree ring-like material structure contributes to the strengthening and toughening of ceramic materials. The bending strength and fracture toughness of the composite are (989±87) MPa and (8.12±0.8) MPa·m1/2, respectively. Compared with single-phase Si3N4, the physical and mechanical properties of Si3N4 ceramics are improved.}
}