@article{Zhang2024, 
author = {Lingjie Zhang and Tingting Zhang and Yunliang Zhao and Guangfeng Dong and Shuaike Lv and Songliang Ma and Shaoxian Song and Mildred Quintana},
title = {Doping engineering of lithium-aluminum layered double hydroxides for high-efficiency lithium extraction from salt lake brines},
year = {2024},
journal = {Nano Research},
volume = {17},
number = {3},
pages = {1646-1654},
keywords = {lithium extraction, salt lake brines, doping engineering, lithium-aluminum layered double hydroxides, density functional theory},
url = {https://www.sciopen.com/article/10.1007/s12274-023-5950-1},
doi = {10.1007/s12274-023-5950-1},
abstract = {Lithium-aluminum layered double hydroxides (LiAl-LDH) have been be successfully applied in commercial-scale for lithium extraction from salt lake brine, however, further advancement of their applications is hampered by suboptimal Li+ adsorption performance and ambiguous extraction process. Herein, a doping engineering strategy was developed to fabricate novel Zn2+-doped LiAl-LDH (LiZnAl-LDH) with remarkable higher Li+ adsorption capacity (13.4 mg/g) and selectivity (separation factors of 213, 834, 171 for Li+/K+, Li+/Na+, Li+/Mg2+, respectively), as well as lossless reusability in Luobupo brine compared to the pristine LiAl-LDH. Further, combining experiments and simulation calculations, it was revealed that the specific surface area, hydrophilic, and surface attraction for Li+ of LiZnAl-LDH were significantly improved, reducing the adsorption energy (Ead) and Gibbs free energy (ΔG), thus facilitating the transfer of Li+ from brine into interface followed by insertion into voids. Importantly, the intrinsic oxygen vacancies derived from Zn-doping depressed the diffusion energy barrier of Li+, which accelerated the diffusion process of Li+ in the internal bulk of LiZnAl-LDH. This work provides a general strategy to overcome the existing limitations of Li+ recovery and deepens the understanding of Li+ extraction on LiAl-LDH.}
}