@article{Song2020, 
author = {Lulu Song and Yuping Duan and Jia Liu and Huifang Pang},
title = {Transformation between nanosheets and nanowires structure in MnO2 upon providing Co2+ ions and applications for microwave absorption},
year = {2020},
journal = {Nano Research},
volume = {13},
number = {1},
pages = {95-104},
keywords = {phase transitions, self-assembly, impedance matching, microwave absorption},
url = {https://www.sciopen.com/article/10.1007/s12274-019-2578-2},
doi = {10.1007/s12274-019-2578-2},
abstract = {The phase transition process of the MnO2 phase with increases in Co2+ doping can be described by the Ouroboros symbol. The undoped sample is pure δ-MnO2 with nanosheets structures. Then a small amount of Co2+ ions changes the final products and generates α-MnO2 nanofibres in the δ-MnO2 matrix. The products become pure α-MnO2 with an appropriate amount of Co added. However, when the Co amount continues to increase, the amount of α-MnO2 decreases in the products and turns back to form pure δ-MnO2 in the end. Analysing the electromagnetic absorption performance, the relationship between the properties and the proportion of δ-MnO2/α-MnO2 in the powders adjusted by Co2+ doping has been explored, and the composites of δ-/α-MnO2 show better absorption ability than the single-phase samples. As a result, the optimal reflection loss (RL) is -54.8 dB, and the effective absorption bandwidth can cover the Ku band at a thickness of 2.2 mm and the X band at a thickness of 3.1 mm with 50 wt.% filler loading ratios. This research might shed new light on the improvement of novel microwave absorption materials.}
}