Barium titanate (BaTiO3, BT) is one of the key dielectric materials for multilayer ceramic capacitor (MLCC) industry. To meet the development trend of miniaturization and high capacity of MLCC, the sintered ceramic with nanosized grain is required. Herein, we demonstrate a controllable preparation of finegrain BaTiO3 ceramic by using sol-gel glass encapsulation strategy to suppress the growth of nanocrystal during sintering. It is found that the BaTiO3 nanocrystal with average lateral particle size of 70 nm and 200 nm (BT70 and BT200) can be coated with Bi2O3-B2O3-SiO2 (BBS) glass shell to form core-shell structures. The fine crystal of barium titanate ceramics can be achieved under different encapsulation quantities and sintering temperature. However, BT70, with a larger specific surface area, higher reactivity, and lower crystallinity, was more prone to hydrolyze in the sol-gel process, leading to the formation of a new phase after sintering, Ba2TiSi2O8, which adversely affected both the sintering behavior and dielectric properties. On the other hand, BT200 exhibited lower possibility to hydrolyze in the sol-gel process, resulting in single-phase ceramics after sintering. When the BT200 coated with 5% (in mass) BBS was sintered at 1100 ℃, a dense BaTiO3 ceramic were obtained, with dielectric constant of 1194.23 and loss of 0.0139 at room temperature and 1 kHz. Therefore, this work provides a robust strategy for suppressing the nanocrystal growth during sintering for MLCC applications.
Zhang J, Hao H, Guo Q, Yao Z, Cao M, Liu H. Dielectric and anti-reduction properties of BaTiO3-based ceramics for MLCC application. Ceram Int 2023;49:24941–7.
Jain A, Wang Y, Shi L. Recent developments in BaTiO3 based lead-free materials for energy storage applications. J Alloys Compd 2022;928:167066.
Chen Y, Li J, Jiang Q, Li A, Yu J, Zeng H. Effect of properties and crystallization behavior of BaO–ZnO–B2O3–SiO2 glass on the electrical conductivity of Cu paste. J Am Ceram Soc 2022;105:5687–97.
Bi K, Bi M, Hao Y, Luo W, Cai Z, Wang X, et al. Ultrafine core-shell BaTiO3@SiO2 structures for nanocomposite capacitors with high energy density. Nano Energy 2018;51:513–23.
Hong K, Lee TH, Suh JM, Yoon SH, Jang HW. Perspectives and challenges in multilayer ceramic capacitors for next generation electronics. J Mater Chem C 2019;7:9782–802.
Li Y, Liu Y, Tang M, Lv J, Chen F, Li Q, et al. Energy storage performance of BaTiO3-based relaxor ferroelectric ceramics prepared through a two-step process. Chem Eng J 2021;419:129673.
Ge P, Liu Z, Huang X, Tang X, Tang Z, Li S, et al. Excellent energy storage properties realized in novel BaTiO3-based lead-free ceramics by regulating relaxation behavior. J Materiomics 2023;9:910–9.
Luan S, Si S, Zhang L, Wang P, Jian G, Yang J, et al. Fabrication of BaTiO3 nanopowders with high tetragonality via two-step assisted rotary furnace calcination for MLCC applications. Ceram Int 2023;49:12529–39.
Luo Z, Hao H, Chen C, Zhang L, Yao Z, Cao M, et al. Hanxing, Dielectric and antireduction properties of (1–x)BaTiO3-xBi(Zn0.5Y0.5)O2.75 ceramics for BME-MLCC application. J Alloys Compd 2019;794:358–64.
Zhu C, Cai Z, Cao X, Fu Z, Li L, Wang X. High-dielectric-constant nanograin BaTiO3-based ceramics for ultra-thin layer multilayer ceramic capacitors via grain grading engineering. Adv Powder Technol 2022;1:100029.
Haily E, Bih L, Lahmar A, Elmarssi M, Manoun B. Effect of BaO–Bi2O3–P2O5 glass additive on structural, dielectric and energy storage properties of BaTiO3 ceramics. Mater Chem Phys 2020;241:122434.
Li T, Segawa H, Ohashi N. Exploration of BaO–B2O3–Bi2O3 glasses as sintering aids for BaTiO3 ceramics. Ceram Int 2020;46:10233–41.
Li T, Segawa H, Ohashi N. Sintering behavior and dielectric properties of BaTiO3 added with BaO-Bi2O3-B2O3 glass phase. Ceram Int 2018;44:13004–10.
Li J, Jiang Q, Yu J, Lin T, Zhang L, Zeng H. Optimizing the size distribution of zinc borosilicate glass powder by organic solvent and tetradecylphosphonic based wet milling. Mater Lett 2023;349:134745.
Su X, Riggs BC, Tomozawa M, Nelson JK, Chrisey DB. Preparation of BaTiO3/low melting glass core–shell nanoparticles for energy storage capacitor applications. J Mater 2014;2:18087–96.
Zheng K, Taccardi N, Beltrán AM, Sui B, Zhou T, Marthala VR, et al. Timing of calcium nitrate addition affects morphology, dispersity and composition of bioactive glass nanoparticles. RSC Adv 2016;6:95101–11.
Abicht H-P, Völtzke D, Schneider R, Woltersdorf J, Lichtenberger O. Defect chemistry of the shell region of water-milled BaTiO3 powders. Mater Chem Phys 1998;55:188-92.
Han JM, Joung MR, Kim JS, Lee YS, Paik JH. Hydrothermal synthesis of BaTiO3 nanopowders using TiO2 nanoparticles. J Am Ceram Soc 2013;97:346–9.
Fan H, Wang G, Hu L. Infrared, Raman and XPS spectroscopic studies of Bi2O3–B2O3–Ga2O3 glasses. Solid State Sci 2009;11:2065–70.
Hashimoto T, Shimoda Y, Nasu H, Ishihara A. ZnO–Bi2O3–B2O3 glasses as molding glasses with high refractive indices and low coloration codes. J Am Ceram Soc 2011;94:2061–6.
Schädli GN, Büchel R, Pratsinis SE. Nanogenerator power output: influence of particle size and crystallinity of BaTiO3. Nanotechnology 2017;28:275705.
Ma R, Cui B, Shangguan M, Wang S, Wang Y, Chang Z, et al. A novel double-coating approach to prepare fine-grained BaTiO3@La2O3@SiO2 dielectric ceramics for energy storage application. J Alloys Compd 2017;690:438–45.
Mhareb MHA, Slimani Y, Alajerami Y, Sayyed M, Lacomme E, Almessiere MA. Structural and radiation shielding properties of BaTiO3 ceramic with different concentrations of Bismuth and Ytterbium. Ceram Int 2020;46:28877–86.
Zhu X, Mai C, Li M. Effects of B2O3 content variation on the Bi ions in Bi2O3–B2O3–SiO2 glass structure. J Non-Cryst Solids 2014;388:55–61.
Xu H, Gao L. Hydrothermal synthesis of high-purity BaTiO3 powders: control of powder phase and size, sintering density, and dielectric properties. Mater Lett 2004;58:1582–6.
Cao S, Jiang B, Zheng Y, Tu X, Xiong K, Gao P, et al. The growth and thermal, electrical properties characterization of Ba2TiSi2O8 piezoelectric crystal. J Cryst Growth 2016;451:207–13.
Masai H, Tsuji S, Fujiwara T, Benino Y, Komatsu T. Structure and non-linear optical properties of BaO–TiO2–SiO2 glass containing Ba2TiSi2O8 crystal. J Non-Cryst Solids 2007;353:2258–62.
Gao Y, Ma J, Che Y, Wang M. Mixed BaO/MgO modifiers effect on structure, thermal and dielectric properties of Bi2O3–B2O3–SiO2–ZnO glasses via sol-gel method. J Mater Sci Mater Electron 2023;34:693.
Qi J, Liu Q, Cao M, Zhao Y, Hao H, Yao Z, et al. A family of functional oxides of titanosilicates: A2TiSi2O8 (A= Ba, Sr) with temperature insensitive ultrahigh breakdown strength. J Eur Ceram Soc 2020;40:3027–34.
Li W, Hao J, Fu P, Du J, Li P, Hu C, et al. Large electrostrictive effect and strong photoluminescence properties in Sm2O3-modified lead-free potassium sodium niobate-based piezoelectric ceramics. J Materiomics 2020;6:768–80.
Maison W, Kleeberg R, Heimann RB, Phanichphant S. Phase content, tetragonality, and crystallite size of nanoscaled barium titanate synthesized by the catecholate process: effect of calcination temperature. J Eur Ceram Soc 2003;23:127–32.
Yao G, Wang X, Yang Y, Li L. Effects of Bi2O3 and Yb2O3 on the curie temperature in BaTiO3-based ceramics. J Am Ceram Soc 2010;93:1697–701.
Liu R, Chen Z, Lu Z, Wang X. Effects of sintering temperature and Bi2O3, Y2O3 and MgO co-doping on the dielectric properties of X8R BaTiO3-based ceramics. Ceram Int 2022;48:2377–84.
Zhang K, Li L, Wang M, Luo W. Charge compensation in rare earth doped BaTiO3-based ceramics sintered in reducing atmosphere. Ceram Int 2020;46:25881–7.
Hudson LT, Kurtz RL, Robey SW, Temple D, Stockbauer RL. Photoelectron spectroscopic study of the valence and core-level electronic structure of BaTiO3. Phys Rev B 1993;47:1174.
Tsai C, Liao W, Chu S, Hong C, Yu M, Lin Y, et al. Investigation of the piezoelectric and anti-reduction properties of (Ba, Ca) (Ti, Sn, Hf) textured ceramics prepared under low oxygen partial pressure conditions at low sintering temperatures. J Eur Ceram Soc 2021;41:2472–81.
This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
京公网安备11010802044758号