In this paper, Sm-doped 0.96(K0.48Na0.52)(Nb0.95Sb0.05)–0.04Bi0.5(Na0.82K0.18)0.5ZrO3 (abbreviated as KNSN–0.04BNKZ) lead-free piezoelectric ceramics were prepared by conventional solid-state sintering method and the effects of Sm2O3 on the phase structure, microstructure, electrical and luminescent properties of KNSN–0.04BNKZ potteries were studied. Results revealed that a single solid solution phase with pseudo-cubic perovskite structure was formed between KNSN–0.04BNKZ and Sm2O3. Existence of weak dielectric/ferroelectric properties with a diffuse dielectric anomaly and slim P–E hysteresis loops of the Sm-doped KNSN–0.04BNKZ demonstrated the ferroelectric relaxor behavior of the KNNS–0.04BNKZ–xSm ceramics. Accordingly, the temperature stability and fatigue behavior of the modified ceramics were significantly improved. It was found that the KNSN–0.04BNKZ ceramics with 0.002 mol Sm addition exhibited nearly temperature independent properties and fatigue-free behavior. Moreover, Sm-modified KNSN–0.04BNKZ exhibits a bright photoluminescence with a strong orange emission under visible light irradiation. As a material with both electrical and luminescent properties, it has good application prospect in future optoelectronic components by integrating its luminescent and electrical properties.
In this paper, Sm-doped 0.96(K0.48Na0.52)(Nb0.95Sb0.05)–0.04Bi0.5(Na0.82K0.18)0.5ZrO3 (abbreviated as KNSN–0.04BNKZ) lead-free piezoelectric ceramics were prepared by conventional solid-state sintering method and the effects of Sm2O3 on the phase structure, microstructure, electrical and luminescent properties of KNSN–0.04BNKZ potteries were studied. Results revealed that a single solid solution phase with pseudo-cubic perovskite structure was formed between KNSN–0.04BNKZ and Sm2O3. Existence of weak dielectric/ferroelectric properties with a diffuse dielectric anomaly and slim P–E hysteresis loops of the Sm-doped KNSN–0.04BNKZ demonstrated the ferroelectric relaxor behavior of the KNNS–0.04BNKZ–xSm ceramics. Accordingly, the temperature stability and fatigue behavior of the modified ceramics were significantly improved. It was found that the KNSN–0.04BNKZ ceramics with 0.002 mol Sm addition exhibited nearly temperature independent properties and fatigue-free behavior. Moreover, Sm-modified KNSN–0.04BNKZ exhibits a bright photoluminescence with a strong orange emission under visible light irradiation. As a material with both electrical and luminescent properties, it has good application prospect in future optoelectronic components by integrating its luminescent and electrical properties.
This work was supported by the National Key R&D Program of China (No. 2016YFB0402701), Innovation Team of Higher Educational Science and Technology Program in Shandong Province (No. 2019KJA025), National Natural Science Foundation of China (Nos. 51701091 and 51802137), Natural Science Foundation of Shandong Province of China (Nos. ZR2018MEM011 and ZR201709270099), Opening Project of Key Laboratory of Inorganic Functional Materials and Devices, Chinese Academy of Sciences (Grant No. KLIFMD201705), and Research Foundation of Liaocheng University (No. 318011906).
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.